进口高压合金管的标准 美标16mn无缝钢管介绍
执行标准
GB6479——化肥设备用高压无缝钢管
GB9948——石油裂化用无缝钢管
ASTM A213 ——Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater, and Heat-Exchanger Tubes
ASTM A335 ——Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service
JIS G3458 ——Alloy Steel Pipes (STPA 12/ 20/ 22/ 23/ 24/ 25/ 26)
JIS G3462 ——Alloy Steel for Boiler and Heat Exchanger Tubes (STBA12/ 13/ 20/ 22)
JIS G3467 ——Steel Tubes for Fired Heater (STF 410/STFA 12/ 22/ 23/ 24/ 25/ 26)
DIN17175-79Ⅲ——Electrical Resistance Or Induction Welded Steel Tubes for Elevated Temperature
主要生产无缝钢管牌号
Cr5Mo (STFA25 STPA25 STBA25 T5 P5)
15CrMo (STFA22 STPA22 STBA22 T12 P12)
1.25Cr0.5Mo (STFA23 STPA23 STBA23 T11 P11)
Cr9Mo (STFA26 STPA26 STBA26 T9 P9)
12Cr1MoV
12Cr2Mo (10CrMo910 T22 P22)
10Cr9Mo1VNb T91 (P91)
12Cr2MoWVTiB (R102)
尺寸公差
查表
力学性能
|
牌号 |
常温力学性能 |
|
标准号 |
钢号 |
σs(MPa) |
σb(MPa) |
δs(%) |
αk(J/cm2) |
|
GB5310 |
12CrMo |
206 |
412-559 |
21 |
69u |
|
15CrMo |
235 |
441-638 |
21 |
59u |
|
12Cr1MoV |
255 |
471-638 |
21 |
59u |
|
12Cr2Mo |
280 |
450-600 |
20 |
|
|
ASTM A335 |
P1 |
207 |
379 |
22 |
|
|
P11 |
207 |
413 |
22 |
|
|
P12 |
207 |
413 |
22 |
|
|
P2 |
207 |
379 |
22 |
|
|
P22 |
207 |
413 |
22 |
|
|
P5 |
207 |
413 |
22 |
|
|
P9 |
207 |
413 |
22 |
|
|
DIN17175 |
19Mn5 |
300-310 |
510-610 |
19 |
|
|
13CrMo44 |
280-290 |
440-590 |
22 |
|
|
14MoV63 |
310-319 |
460-610 |
20 |
|
|
10CrMo910 |
269-280 |
450-600 |
|
|
|
JIS G3458 |
STPA12 |
206 |
382 |
|
|
|
STPA20 |
206 |
412 |
|
|
|
STPA22 |
206 |
412 |
|
|
|
STPA23 |
206 |
412 |
|
|
|
STPA24 |
206 |
412 |
|
|
|
STPA25 |
206 |
412 |
|
|
|
STPA26 |
206 |
412 |
|
|
|
JIS G3462 |
STBA12 |
206 |
382 |
|
|
|
STBA13 |
206 |
412 |
|
|
|
STBA22 |
206 |
412 |
|
|
|
STBA20 |
206 |
412 |
|
|
|
STBA23 |
206 |
412 |
|
|
化学成分
|
牌号 |
化学成分(%) |
|
标准号 |
钢号 |
C |
Mn |
Si |
Cr |
Mo |
V |
S |
P |
|
GB5310 |
12CrMo |
0.08-0.15 |
0.40-0.70 |
0.17-0.37 |
0.40-0.70 |
0.40-0.55 |
|
≤0.035 |
≤0.035 |
|
15CrMo |
0.12-0.18 |
0.40-0.70 |
0.17-0.37 |
0.80-1.10 |
0.40-0.55 |
|
≤0.035 |
≤0.035 |
|
12Cr1MoV |
0.08-0.15 |
0.40-0.70 |
0.17-0.37 |
0.90-1.20 |
0.25-0.35 |
0.15-0.30 |
≤0.035 |
≤0.035 |
|
12Cr2Mo |
0.08-0.15 |
0.40-0.70 |
≤0.50 |
2.00-2.50 |
0.90-1.20 |
|
≤0.035 |
≤0.035 |
|
ASTM A335 |
P1 |
0.10-0.20 |
0.30-0.80 |
0.10-0.50 |
|
0.44-0.65 |
|
≤0.045 |
≤0.045 |
|
P11 |
≤0.15 |
0.30-0.60 |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
≤0.030 |
≤0.030 |
|
P12 |
≤0.15 |
0.30-0.61 |
≤0.50 |
0.80-1.25 |
0.44-0.65 |
|
≤0.045 |
≤0.045 |
|
P2 |
0.10-0.20 |
0.30-0.61 |
0.10-0.30 |
0.50-0.81 |
0.44-0.65 |
|
≤0.045 |
≤0.045 |
|
P22 |
≤0.15 |
0.30-0.60 |
≤0.50 |
1.90-2.60 |
0.87-1.13 |
|
≤0.030 |
≤0.030 |
|
P5 |
≤0.15 |
0.30-0.60 |
≤0.50 |
4.00-6.00 |
0.45-0.65 |
|
≤0.030 |
≤0.030 |
|
P9 |
≤0.15 |
0.30-0.60 |
0.25-1.00 |
8.00-10.00 |
0.90-1.10 |
|
≤0.030 |
≤0.030 |
|
DIN17175 |
19Mn5 |
0.17-0.22 |
1.00-1.30 |
0.30-0.60 |
≤0.30 |
|
|
≤0.04 |
≤0.04 |
|
13CrMo44 |
0.10-0.18 |
0.40-0.70 |
0.10-0.35 |
0.70-1.10 |
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
14MoV63 |
0.10-0.18 |
0.40-0.70 |
0.10-0.35 |
0.30-0.60 |
0.50-0.70 |
0.22-0.32 |
≤0.035 |
≤0.035 |
|
10CrMo910 |
0.08-0.15 |
0.40-0.70 |
≤0.50 |
2.00-2.50 |
0.90-1.20 |
|
≤0.035 |
≤0.035 |
|
JIS G3458 |
STPA12 |
0.10-0.20 |
0.30-0.80 |
0.10-0.50 |
|
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STPA20 |
0.10-0.20 |
0.30-0.60 |
0.10-0.50 |
0.50-0.80 |
0.40-0.65 |
|
≤0.035 |
≤0.035 |
|
STPA22 |
≤0.15 |
0.30-0.60 |
≤0.50 |
0.80-1.25 |
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STPA23 |
≤0.15 |
0.30-0.60 |
≤0.50 |
0.80-1.25 |
0.45-0.65 |
|
≤0.030 |
≤0.030 |
|
STPA24 |
≤0.15 |
0.30-0.60 |
≤0.50 |
1.90-2.60 |
0.87-1.13 |
|
≤0.030 |
≤0.030 |
|
STPA25 |
≤0.15 |
0.30-0.60 |
≤0.50 |
4.00-6.00 |
0.45-0.65 |
|
≤0.030 |
≤0.030 |
|
STPA26 |
≤0.15 |
0.30-0.60 |
0.25-1.00 |
8.00-10.00 |
0.90-1.10 |
|
≤0.030 |
≤0.030 |
|
JIS G3462 |
STBA12 |
0.10-0.20 |
0.30-0.80 |
0.10-0.50 |
|
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA13 |
0.15-0.25 |
0.30-0.80 |
0.10-0.50 |
|
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA22 |
≤0.15 |
0.30-0.60 |
≤0.50 |
0.80-1.25 |
0.45-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA20 |
0.10-0.20 |
0.30-0.60 |
0.10-0.50 |
0.50-0.80 |
0.40-0.65 |
|
≤0.035 |
≤0.035 |
|
STBA23 |
≤0.15 |
0.30-0.60 |
0.50-1.00 |
1.00-1.50 |
0.45-0.65 |
|
|
|
进口高压合金管的标准 美标16mn无缝钢管介绍
16Mn低合金管
16Mn合金管
16Mn叫低合金高强度结构钢
低合金高强度结构钢：含碳量为0.1%-0.25%,加入主要合金元素锰、硅、钒、铌和钛等；它的含合金总量<3%。按强度分为300、350、400和450MPa等4个级别。主要有Q295、Q345、Q390、Q420、Q460。“Q”是屈服的“屈”字的汉语拼音大写字头，其后数字为该牌号最小屈服点(σs)值，其后的符号是按照该钢杂质元素(硫、磷)含量由高到低并伴随碳、锰元素的变化而分为A、B、C、D四等。其中A、B级钢通常称16Mn。
化学成分：C：0.12-0.20；Mn：1.20-1.60；Si：0.20-0.55；
抗拉强度：470-660牛/平方毫米；
屈服强度：275-345牛/平方毫米；
伸长率：21%。具体值要根据钢材的厚度或直径，以上数据对应钢材的厚度或直径为：16-100mm
用途：用于桥梁的专用钢种为“16Mnq”，汽车大梁的专用钢种为“16MnL”，压力容器的专用钢种为“16MnR”。
16Mn
16Mn是钢材的一种材质。16Mn是过去的叫法，现在的称为：Q345
16：代表这种钢材中碳的含量在0.16%左右。
Mn：单独提出来,是因为五大元素(碳C，硅Si，锰Mn，磷P，硫S)中,锰的含量高,大约在1.20-1.60%左右。
16Mn属低合金钢板系列，在此系列中，为最普通材质，或者牌号的钢板。
根据特殊的要求，可以对钢板进行一些特殊的处理：热处理和Z向性能。
◆ 热处理：控轧，正火等等。
◆ Z向性能：Z15，Z25，Z35
主要特性：
综合性能好，低温性能好，泠冲压性能，焊接性能和可切削性能好。
应用举例：
矿山，运输，化工等各种机械。
16Mn化学成分及力学性能
16Mn化学成分
|
牌号 |
化学成分(质量分数)(%) |
|
C |
Si |
Mn |
P≤ |
S≤ |
Cr |
Mo |
V |
|
16Mn |
0.12-0.20 |
0.20-0.60 |
1.20-1.60 |
0.030 |
0.030 |
- |
- |
- |
16Mn力学性能
|
牌号 |
拉力强度MPa |
屈服点MPa |
伸长率(%) |
|
16Mn |
490-670 |
320 |
21 |
16Mn锻件的化学成分
|
牌号 |
化学成分(质量分数)(%) |
|
C
≤ |
Si
≤ |
Mn |
P
≤ |
S
≤ |
Nb |
Ti |
V |
|
Q345(16Mn)
低合金高强度结构钢 |
0.20% |
0.55% |
1.00%-1.60 |
0.045% |
0.045% |
0.015%-0.060% |
0.02%-0.20% |
0.02%-0.15% |
16Mn锻件的力学性能：
|
公称壁厚 |
热处理状态 |
拉伸试验σb |
冲击试验 |
硬度试验HB |
物理性质 |
应用举例 |
|
≤300 mm |
正火，
正火+回火
回火温度℃≥600 |
450-600 MPa；
σs≥275 MPa；
δ5≥20% |
试验温度0℃；
Akv ,
J≥31 |
121-178 |
综合力学性能好，焊接
性、冷、热加工性能和耐
蚀性能均好，C、D、E
级钢具有良好的低温韧
性。 |
船舶，锅炉，压
力容器，石油储
罐，桥梁，电站
设备。起重运输
机械及其他较高
载荷的焊接结构
件。 |
|